PA6 BKV 30 H2.0 EF DUS029 901510德國朗盛Durethan 30%玻纖增強尼龍6塑料（18024445500）

PA 6, 30 % glass fibers, injection molding, improved flowability, heat-aging stabilized



ISO Shortname: ISO 1874-PA 6,MHR,12-090,GF30

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.23　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.70　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.05　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.14　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 9500　
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 155　
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.9　
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 65　
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 50　
Izod impact strength 23 °C kJ/m² ISO 180-1U 60　
Izod impact strength -30 °C kJ/m² ISO 180-1U 50　
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 10　
Izod notched impact strength -30 °C kJ/m² ISO 180-1A <10　

Thermal properties
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 205　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 220　
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.2　
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.9